provides high-resistance, rubber-like properties, allowing it to bend and snap back into shape, unlike brittle standard PLA. These filaments often feature an elongation at break of up to 300% and high tensile strength. They are ideal for durable, shock-absorbing components, including wearables and protective covers, while often being easier to print than standard flexible materials like
| Diameter: | 1.75mm |
| Tolerance: | ยฑ0.02mm |
| Material Density | 1.17-1.30g/cm3 ย |
| Tensile Strength | 47Mpa |
| Tensile Strength๏ผprinted๏ผ | โฅ34Mpa |
| Elongation at Break | 300% |
| Impact intensity (KJ/M,Izod2) | ย 1-3 |
| Vicat softening point | 70โ |
| Melting Index(g/10min) | 4-6(190โ,2.15kg) |
| Melting Point | 178.5โ |
| Printing Temperature | 190-220โ |
| Hot Pad Temperature | 40-60โ |
| Max Volumetric Speed | 20-21(mmยณ/s๏ผ |